Aluminum sheets 5052 H32 mill finish ASTM B209 standard sheet metal
ASTM B209 Standard Flat Aluminum Sheet Alloy 5052 H34 Aluminum Magnesium
| Chemical Composition % 5052 ALUMINUM SHEET |
| Alloy No. | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | V | Ti | Zr | Al |
| 5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | - | 0.1 | - | - | - | Remainder |
| Properity of 5052 H32 ALUMINUM SHEET |
Alloy
Temper | Specified thickness | Tensile
strength | Yield
strength | Elongation |
| (MPa) | (MPa) | (%) |
| 5052/H32 | 0.4-0.63mm | 214-262 | min 159 | min 4 |
| 0.63-1.2mm | min 5 |
| 1.2-6.3mm | min 7 |
| 6.3-50mm | min 11 |
Description of 5052 aluminum sheet:
5052 aluminum sheet is often referred to as "Anodize Quality Aluminum", as it has excellent finishing qualities and anodized coatings are bright and clear. The major alloying element in 5052 (aluminum sheet) is magnesium in sufficient quantities to cause substantial lowering of the melting point without producing brittleness. When magnesium is used as the major alloying element, or in combination with manganese, the result is a moderate to high strength non-heat treatable aluminum alloy. 5052 aluminum sheet is far stronger than the 1100 or 3000 series aluminums, yet forms with reasonable bend radii. Weldability is very good and 5052 aluminum sheet has good resistance to corrosion, especially in salt-water / marine atmospheres.
Applications of 5052 aluminum sheet:
5052 aluminum sheet is widely used for cooking utensils, food processing equipment, storage tanks, truck and trailer components, mail boxes, aircraft components, electronic chassis, boat hulls, deck houses, hatch covers, pressure vessels, ladders, railings, frames, drip pans, tool boxes, truck bumpers, inner and outer body panels and components in truck and auto industries, kitchen equipment, decorative trim, architectural uses, signage applications, and any number of parts and application requiring strength and good formability at reasonable cost.
Storage of aluminum sheet: