Industrial pure aluminum 0.2-6mm H14 H16 H18 O 1050 Aluminum Sheet
Aluminum alloy 1050 is industrial pure aluminum, with high plasticity, corrosion resistance, electrical conductivity and thermal conductivity, but low strength, heat treatment can not strengthen the cutting is not good; Gas welding, hydrogen welding and contact welding, not easy brazing; Easy to bear all kinds of pressure processing and extension, bending.
| Conditions | Tensile Properties |
| T (°C) | Treatment |
| 25 | H14 | Tensile Strength (MPa) | 110 |
| Yield Strength (MPa) | 105 |
| Elongation (%) | |
| Reduction in Area (%) | |
| 25 | H16 | Tensile Strength (MPa) | 130 |
| Yield Strength (MPa) | 125 |
| Elongation (%) | |
| Reduction in Area (%) | |
| 25 | H18 | Tensile Strength (MPa) | 160 |
| Yield Strength (MPa) | 145 |
| Elongation (%) | |
| Reduction in Area (%) | |
| 25 | O | Tensile Strength (MPa) | 76 |
| Yield Strength (MPa) | 28 |
| Elongation (%) | |
| Reduction in Area (%) | |
The 1050 aluminum alloy is formed by adding a small amount of copper to pure aluminum, with excellent forming characteristics, high corrosion resistance, good welding and electrical conductivity. It is widely used in products with low strength requirements, such as chemical instruments, thin plate workpieces, deep drawing or spinning concave vessels, welding parts, heat exchangers, clock surfaces and dish surfaces, nameplates, kitchenware, ornaments, reflectors and so on.