Pure Aluminum Alloy 1060 O / H12 /H16 / H18 / H24 Aluminum Sheet For Nameplate
Product introduction of 1060 Aluminum Sheet:
1060 aluminum is a 1000-series aluminum alloy: it is considered commercially pure, and is formulated for primary forming into wrought products. 1060 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-1060. A91060 is the UNS number. Additionally, the EN chemical designation is Al99.6.
Product Details of Aluminum Sheet:
Alloy : 1060
Temper: O, H12, H14, H16, H18, H22, H24, H26, H28 and etc.
Material: direct chill cast (DC) or Continuous cast(CC)
Thickness: 0.2mm-6.35mm
Width: 200mm-2650mm
Length: ≤12000mm
Mechanical Property Specification of 1060 Aluminum Sheet:
| Elements | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others | Al |
| Content | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | - | 0.05 | 0.03 | 0.15 | Remain |
| (max) |
| Alloy | Specified | Tensile | Yield | Elongation |
| Temper | strength | strength |
| | Thickness(in.) | (ksi) | (ksi) | (%) |
| 1060-O | 0.006-0.019 | 8.0-14.0 | 2.5 | Min15 |
| (annealed) | 0.020-0.050 | Min22 |
| | 0.051-3.000 | Min25 |
| 1060-H12/ | 0.017-0.050 | 11.0-16.0 | 9 | Min6 |
| 1060-H22 | 0.051-2.000 | Min12 |
| 1060-H14/ | 0.006-0.019 | 12.0-17.0 | 10 | Min1 |
| 1060-H24 | 0.020-0.050 | Min5 |
| | 0.051-1.000 | Min10 |
| 1060-H16/ | 0.006-0.019 | 14.0-19.0 | 11 | Min1 |
| 1060-H26 | 0.020-0.050 | Min4 |
| | 0.051-0.162 | Min5 |
| 1060-H18/ | 0.006-0.019 | Min16.0 | Min12.0 | Min1 |
| 1060-H28 | 0.020-0.050 | Min3 |
| | 0.051-0.128 | Min4 |
| | 0.250-0.499 | Min11.0 | Min7.0 | Min10 |
| 1060-H112 | 0.500-1.000 | Min10.0 | Min5.0 | Min20 |
| | 1.001-3.000 | Min9.0 | Min4.0 | Min25 |
| Principal Design Features | This is a relatively low strength, essentially pure aluminum, alloy. It is noted for excellent welding characteristics and formability along with good corrosion resistance. It cannot be hardened by heat treatment. |
| Applications | Commonly used in the manufacture of chemical equipment and railroad tank cars. |
| Machinability | The machinability of AL 1060 is fair to poor, especially in the soft temper conditions. In the harder (cold worked) tempers such as H16 and H18 the machining characteristics are improved. Either carbide or high-speed steel tooling may be used and use of lubricants is recommended, although some cutting may be done dry. |
| Forming | This alloy has excellent forming capability by cold or hot working with commercial techniques. |
| Welding | AL 1060 may be welded by standard commercial methods. If filler rod is required it should be of AL 1060. A precaution should be noted for the use of resistance welding as by this method some trial and error experimentation may be required to obtain good results. |
Applications of 1060 Aluminum Sheet:
Clock surface and nameplate and eetc.