High Pure 1145 Aluminium Alloy For Foil Stock And Cable Aluminum Products
Product introduction of 1145 Aluminum Sheet:
Aluminium / Aluminum alloys are known for their strong corrosion resistance. They are sensitive to high temperatures in the range of 200 to 250°C (392 to 482°F). High temperatures tend to reduce these alloys’ strength. However, the strength of the aluminum alloys can be increased at subzero temperatures, making them good low-temperature alloys.
Product Details of Aluminum Sheet:
Alloy : 1145
Temper: O, H18, H19 and etc.
Material: direct chill cast (DC) or Continuous cast(CC)
Thickness: 0.2mm-6.35mm
Width: 200mm-2650mm
Length: ≤12000mm
Property Specification of 1145 Aluminum Sheet:
| Physical Properties | Metric | English | Comments |
| Density | 2.70 g/cc | 0.0975 lb/in³ | AA; Typical |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 21 | 21 | 500 kg load with 10 mm ball. Calculated value. |
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | / |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | / |
| Elongation at Break | 2.40% | 2.40% | Foil |
| | 40% | 40% | In 5 cm |
| Thickness 1.60 mm | Thickness 0.0630 in |
| Modulus of Elasticity | 69.0 GPa | 10000 ksi | In Tension; Compressive Modulus is about 2% higher |
| Poissons Ratio | 0.33 | 0.33 | |
| Shear Modulus | 26.0 GPa | 3770 ksi | Calculated |
| Shear Strength | 55.0 MPa | 7980 psi | Calculated value. |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.00000280 ohm-cm | 0.00000280 ohm-cm | / |
Forming of 1145 Aluminum Sheet:
Aluminium / Aluminum 1145 alloy has excellent forming quality and can be easily formed using all the conventional forming methods.
Welding of 1145 Aluminum Sheet:
Weldability of the Aluminium / Aluminum 1145 alloy is excellent when commercial methods such as TIG or MIG welding are used.
Applications of 1145 Aluminum Alloy: